Högskolan i Skövde

The aim of the present study was to investigate the tool performance when machining compacted graphite iron (CGI) alloys. A comparison was made between solid solution strengthened CGI including various amounts of silicon (Si-CGI) and the pearlitic-ferritic CGI as a reference material. The emphasis was on examining the influence of microstructure and mechanical properties of the material on tool wear in face milling process. Machining experiments were performed on the engine-like test pieces comprised of solid solution strengthened CGI with three different silicon contents and the reference CGI alloy. The results showed up-to 50% lower flank wear when machining Si-CGI alloys, although with comparable hardness and tensile properties. In-depth analysis of the worn tool surfaces showed that the abrasion and adhesion were the dominant wear mechanisms for all investigated alloys. However, the better tool performance when machining Si-CGI alloys was mainly due to a lower amount of abrasive carbo-nitride particles and the suppression of pearlite formation in the investigated solid solution strengthened alloys.

This study focuses on the modelling and simulation of local mechanical properties of compacted graphite iron cast at different section thicknesses and three different levels of silicon, ranging from about 3.6% up to 4.6%. The relationship between tensile properties and microstructure is investigated using microstructural analysis and statistical evaluation. Models are generated using response surface methodology, which reveal that silicon level and nodularity mainly affect tensile strength and 0.2% offset yield strength, while Young′s modulus is primarily affected by nodularity. Increase in Si content improves both the yield and tensile strength, while reduces elongation to failure. Furthermore, mechanical properties enhance substantially in thinner section due to the high nodularity. The obtained models have been implemented into a casting process simulation, which enables prediction of local mechanical properties of castings with complex geometries. Very good agreement is observed between the measured and predicted microstructures and mechanical properties, particularly for thinner sections.

Numerical simulations of component behavior and performance is critical to develop optimized and robust load-bearing components. The reliability of these simulations depend on the description of the components material behavior, which for e.g. cast and polymeric materials exhibit component specific local variations depending on geometry and manufacturing parameters. Here an extension of a previously presented strategy, the closed chain of simulations for cast components, to predict and incorporate local material data into Finite Element Method (FEM) simulations on multiple scales is shown. Manufacturing process simulation, solidification modelling, material characterization and representative volume elements (RVE) provides the basis for a microstructure-based FEM analysis of component behavior and a simulation of the mechanical behavior of the local microstructure in a critical region. It is discussed that the strategy is applicable not only to cast materials but also to injection molded polymeric materials, and enables a common integrated computational microstructure-based approach to optimized components.

The mechanical behaviour and performance of a ductile iron component is highly dependent on the local variations in solidification conditions during the casting process. Here we show a framework which combine a previously developed closed chain of simulations for cast components with a micro-scale Finite Element Method (FEM) simulation of the behaviour and performance of the microstructure. A casting process simulation, including modelling of solidification and mechanical material characterization, provides the basis for a macro-scale FEM analysis of the component. A critical region is identified to which the micro-scale FEM simulation of a representative microstructure, generated using X-ray tomography, is applied. The mechanical behaviour of the different microstructural phases are determined using a surrogate model based optimisation routine and experimental data. It is discussed that the approach enables a link between solidification- and microstructure-models and simulations of as well component as microstructural behaviour, and can contribute with new understanding regarding the behaviour and performance of different microstructural phases and morphologies in industrial ductile iron components in service.